Eco-friendly Electronics UV Conformal Coating Adhesive with Chip Protection and for Certification for Anti-Friction Applications

Eco-friendly Electronics UV Conformal Coating Adhesive with Chip Protection and for Certification for Anti-Friction Applications

● After being exposed to ultraviolet light and undergoing a moisture polymerization reaction, the product forms a transparent, dense and smooth coating with excellent flexibility, wear resistance, and electrical insulation properties. It exhibits excellent corrosion resistance, moisture resistance, and mold resistance in environments such as salt spray, acid-base, sulfurization, and hot humid conditions.
● Compliant with the relevant requirements of the EU RoHS Directive and REACH regulations,

Sales Count 0 Click

Sales Count 0

Click

Select the number of specifications

UV and moisture dual-curing anti-corrosion paint

100g

Please check the product information you want!

Specifications select

Product Detail Parameters

Parameters

商品规格：4kg

Technical parameters of liquid three-proof adhesive
NO.	Project	Indicator	Inspection method
1	Appearance	Light yellow viscous liquid	Visual inspection
2	Specific gravity (25℃)	1.050±0.03	GB 1756-1979
3	Viscosity (mPa · s)	160±80	GB/T9751-1998
4	Solid content (Wt%)	99±1	Enterprise standard
5	Recommended coating thickness (dry film, µm)	≥80	IPC-CC-830B.4.6.4
Technical parameters of the three-proof adhesive after curing
NO.	Project	Indicator	Inspection method
6	Adhesion (100-grid test)	Level 0	Refer to GB/T9286-1998 for the cross-cutting test of paint films on paints and varnishes
7	Salt spray resistance (35℃, 5%NaCl solution, 192 hours)	There are no adverse phenomena such as bubbling, peeling or wrinkling, and the substrate is not corroded.	Test Ka: Salt spray test Method in accordance with GB/T2423.17-2008 Basic Environmental Test Procedures for Electronic and Electrical Products
8	Water absorption rate (%)	≤1	Refer to HG/T 3856-2006 'Determination Method of Water Absorption Rate of Insulating Paint Film
9	Flame retardant grade (UL94 V-0)	Conforms to	Chapter 8 of UL94-2006 stipulates
10	Solidified energy	1200mj/cm2-1500mj/cm2	Enterprise standard

No comment

Previous : Strong Bonding UV Curing Adhesive for Electronic Components , Moisture-Proof Non-Corrosive Fixing Glue Next : CHINA Source Factory UV-conformal Coating Anti-mildew, anti-corrosion, and moisture-proof apply Instruments and Meters

Parameters

商品规格：4kg

Product Detail

Technical parameters of liquid three-proof adhesive
NO.	Project	Indicator	Inspection method
1	Appearance	Light yellow viscous liquid	Visual inspection
2	Specific gravity (25℃)	1.050±0.03	GB 1756-1979
3	Viscosity (mPa · s)	160±80	GB/T9751-1998
4	Solid content (Wt%)	99±1	Enterprise standard
5	Recommended coating thickness (dry film, µm)	≥80	IPC-CC-830B.4.6.4
Technical parameters of the three-proof adhesive after curing
NO.	Project	Indicator	Inspection method
6	Adhesion (100-grid test)	Level 0	Refer to GB/T9286-1998 for the cross-cutting test of paint films on paints and varnishes
7	Salt spray resistance (35℃, 5%NaCl solution, 192 hours)	There are no adverse phenomena such as bubbling, peeling or wrinkling, and the substrate is not corroded.	Test Ka: Salt spray test Method in accordance with GB/T2423.17-2008 Basic Environmental Test Procedures for Electronic and Electrical Products
8	Water absorption rate (%)	≤1	Refer to HG/T 3856-2006 'Determination Method of Water Absorption Rate of Insulating Paint Film
9	Flame retardant grade (UL94 V-0)	Conforms to	Chapter 8 of UL94-2006 stipulates
10	Solidified energy	1200mj/cm2-1500mj/cm2	Enterprise standard

Copy product links

Long by picture save/share

INQUIRY

Send your message to us MORE+

Contact *
Phone *
Message
Submit

Security Code

Refresh the code

Cancel

Confirm

Inquiry Content：

You have no items to require

Add Successfully

Continue To Visit Inquiry Now